Self-replicating cracks: a collaborative fracture mode in thin films

Abstract

Straight cracks are observed in thin coatings under residual tensile stress, resulting into the classical network pattern observed in china crockery, old paintings or dry mud. Here, we present a novel fracture mechanism where delamination and propagation occur simultaneously, leading to the spontaneous self-replication of an initial template. Surprisingly, this mechanism is active below the standard critical tensile load for channel cracks and selects a robust interaction length scale on the order of 30 times the film thickness. Depending on triggering mechanisms, crescent alleys, spirals or long bands are generated over a wide range of experimental parameters. We describe with a simple physical model the selection of the fracture path and provide a configuration diagram displaying the different failure modes.

References in corpus (1)

• Development and geometry of isotropic and directional shrinkage crack patterns

Cited by in corpus (5)

• Physics of drying complex fluid drop: flow field, pattern formation, and desiccation cracks
• A new failure mechanism in thin film by collaborative fracture and delamination: interacting duos of cracks
• Tearing of thin sheets: Cracks interacting through an elastic ridge
• Crosslinking degree variations enable programming and controlling soft fracture via sideways cracking
• The Physics of Drying of Colloidal Dispersion: Pattern Formation and Desiccation Cracks