Structure and stability of the Si(105) surface
arXiv:cond-mat/0306547 · doi:10.1016/j.susc.2003.08.028
Abstract
Recent experimental studies have shown that well-annealed, unstrained Si(105) surfaces appear disordered and atomically rough when imaged using scanning tunnelling microscopy (STM). We construct new models for the Si(105) surface that are based on single- and double-height steps separated by Si(001) terraces, and propose that the observed surface disorder of Si(105) originates from the presence of several structural models with different atomic-scale features but similar energies. This degeneracy can be removed by applying compressive strains, a result that is consistent with recent observations of the structure of the Ge/Si(105) surface.
4 figures, 1 table