Dynamics of alpha- and beta- processes in thin polymer films: poly(vinyl acetate) and poly(methyl methacrylate)

Abstract

Dynamics of thin films of poly(vinyl acetate) (PVAc) and poly(methyl methacrylate) (PMMA) have been investigated by dielectric relaxation spectroscopy in the frequency range from 0.1Hz to 1MHz at temperatures from 263K to 423K. The $\alpha$-process, the key process of glass transition, is observed for thin films of PVAc and PMMA as a dielectric loss peak at a temperature $T_{\alpha }$ in temperature domain with a fixed frequency. For PMMA the $\beta$-process is also observed at a temperature $T_{\beta }$. For PVAc, $T_{\alpha }$ decreases gradually with decreasing thickness, and the thickness dependence of $T_{\alpha }$ is almost independent of the molecular weight ($M_{\mathrm{w}}\le 2.4\times 10^5$). For PMMA, $T_{\alpha }$ remains almost constant as thickness decreases down to a critical thickness $d_c$, at which point it begins to decrease with decreasing thickness. Contrastingly, $T_{\beta }$ decreases gradually as thickness decreases to $d_c$, and below $d_c$ it decreases drastically. For both PVAc and PMMA, the broadening of the distribution of the relaxation times in thinner films is observed and this broadening is more pronounced for the $\alpha$-process than for the $\beta$-process. It is also observed that the relaxation strength is depressed as the thickness decreases for both the polymers.

11 pages, 12 figures, 1 table

References in corpus (1)

• Slow dynamics near glass transitions in thin polymer films

Cited by in corpus (7)

• Glass transition and alpha-relaxation dynamics of thin films of labeled polystyrene
• Aging phenomena in PMMA thin films -- memory and rejuvenation effects
• Local Dielectric Spectroscopy of Nanocomposite Materials Interfaces
• Local dielectric spectroscopy of near-surface glassy polymer dynamics
• Molecular Dynamics in grafted layers of poly(dimethylsiloxane) (PDMS)
• Crossover of aging dynamics in polymer glass: from cumulative aging to non-cumulative aging
• Reorientation dynamics in thin glassy films