Superconducting Hydride Mg2RhH6 Experimentally Achieved at Lower Pressure

Abstract

Although tremendous progress has been made in recent years in the field of polyhydride superconductors, the realization of high critical temperature superconductivity still relies on formidable high pressures. Searching for superconducting hydrides at lower pressures is of particular importance. Here we report the first experimental synthesis of the Mg2RhH6, which achieves superconductivity under a significantly reduced pressure of 30 GPa. The synthesis of Mg2RhH6 proceeds via a two step process (1) preparation of the Mg2RhH5 precursor containing hydrogen atoms stabilized by covalent bonds, followed by (2) hydrogen supplementation resulting in the filling of electrons into anti bonding orbitals above 30 GPa, which was accompanied by the structural transition from RhH5 square pyramid to RhH6 octahedron. Superconductivity is achieved at 30 GPa with a Tc of 24 K, which is further enhanced to 29 K at 53 GPa, evidenced by a sharp drop of resistivity to zero and characteristic suppression of Tc under applied magnetic fields. Our experiments prove the Mg2RhH6 superconductor to be thermodynamically stable above 30 GPa, making it the first case exhibiting a Tc of approximately 30 K at a readily accessible pressure. This study pioneers a highly promising pathway for the rational design and discovery of high temperature superconductors within phonon mediated BCS framework.

25 pages, 5 figures

References in corpus (15)

• Conventional superconductivity at 203 K at high pressures
• Superconductivity at 250 K in lanthanum hydride under high pressures
• Superconductivity above 200 K Observed in Superhydrides of Calcium
• Prediction of high-Tc superconductivity in ternary lanthanum borohydrides
• Feasible route to high-temperature ambient-pressure hydride superconductivity
• Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures
• Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds
• Superconductivity above 70 K observed in lutetium polyhydrides
• Record High Tc Element Superconductivity Achieved In Titanium
• Superconductivity in Zirconium Polyhydrides with Tc above 70 K
• Prediction of ambient pressure superconductivity in cubic ternary hydrides with MH${}_6$ octahedra
• Superconductivity Observed in Tantalum Polyhydride at High Pressure
• Superconductivity Discovered in Niobium Polyhydride at High Pressures
• Superconductivity with Tc 116K discovered in antimony polyhydrides
• High Pressure Superconducting transition in Dihydride BiH${}_2$ with Bismuth Open-Channel Framework