Percolating Corrosion Pathways of Chemically Ordered NiCr Alloys in Molten Salts
arXiv:2510.25098 · doi:10.1016/j.corsci.2026.113960
Abstract
Recent experiments have shown that chemical ordering in NiCr alloys can significantly accelerate corrosion in molten salt environments. However, the underlying mechanisms remain poorly understood. Using reactive molecular dynamics and first-principles calculations, we show that long-range ordered NiCr in Ni-33at.%Cr alloys corrodes far more rapidly in FLiNaK salt at 800°C than short-range ordered or random solid solutions. This accelerated attack originates from percolating Cr pathways that enhance near-surface diffusion and a lowered energetic barrier for Cr dissolution, as confirmed by first-principles calculations. Contrary to earlier explanations that attributed this behavior to residual stresses, our stress-free simulations demonstrate that ordering alone accelerates the degradation. These results establish percolation as a critical link between chemical ordering and corrosion kinetics, offering a mechanistic basis for experimental observations.
8 figures
References in corpus (4)
- One Dimensional Wormhole Corrosion in Metals
- A Reactive Force Field Approach to Modeling Corrosion of NiCr Alloys in Molten FLiNaK Salts
- First-Principles Investigation of Grain Boundary Effects on Fluorine-Induced Initial Corrosion of NiCr Alloys
- Surface Orientation-dependent Corrosion Behavior of NiCr Alloys in Molten FLiNaK Salt