CMOS-compatible photonic integrated circuits on thin-film ScAlN

Abstract

Scandium aluminum nitride (ScAlN) has recently emerged as an attractive material for integrated photonics due to its favorable nonlinear optical properties and compatibility with CMOS fabrication. Despite the promising and versatile material properties, it is still an outstanding challenge to realize low-loss photonic circuits on thin-film ScAlN-on-insulator wafers. Here, we present a systematic study on the material quality of sputtered thin-film ScAlN produced in a CMOS-compatible 200 mm line, and an optimized fabrication process to yield 400 nm thick, fully etched waveguides. With surface polishing and annealing, we achieve micro-ring resonators with an intrinsic quality factor as high as $1.47\times 10^5$, corresponding to a propagation loss of 2.4 dB/cm. These results serve as a critical step towards developing future large-scale, low-loss photonic integrated circuits based on ScAlN.

References in corpus (8)

• Deep Learning with Coherent Nanophotonic Circuits
• Integrated photonics on thin-film lithium niobate
• Microresonator Soliton Dual-Comb Spectroscopy
• AlScN: A III-V semiconductor based ferroelectric
• Low-loss, silicon integrated, aluminum nitride photonic circuits and their use for electro-optic signal processing
• Aluminum nitride as a new material for chip-scale optomechanics and nonlinear optics
• Tunable optoelectronic and ferroelectric properties in Sc-based III-nitrides
• Pockels Soliton Microcomb

Cited by in corpus (1)

• Piezoelectric actuation for integrated photonics