Vanishing of the anomalous Hall effect and enhanced carrier mobility in the spin-gapless ferromagnetic Mn2CoGa1-xAlx alloys

arXiv:2311.18335 · doi:10.1063/5.0170937

Abstract

Spin gapless semiconductor (SGS) has attracted long attention since its theoretical prediction, while concrete experimental hints are still lack in the relevant Heusler alloys. Here in this work, by preparing the series alloys of Mn2CoGa1-xAlx (x=0, 0.25, 0.5, 0.75 and 1), we identified the vanishing of anomalous Hall effect in the ferromagnetic Mn2CoGa (or x=0.25) alloy in a wide temperature interval, accompanying with growing contribution from the ordinary Hall effect. As a result, comparatively low carrier density (1020 cm-3) and high carrier mobility (150 cm2/Vs) are obtained in Mn2CoGa (or x=0.25) alloy in the temperature range of 10-200K. These also lead to a large dip in the related magnetoresistance at low fields. While in high Al content, despite the magnetization behavior is not altered significantly, the Hall resistivity is instead dominated by the anomalous one, just analogous to that widely reported in Mn2CoAl. The distinct electrical transport behavior of x=0 and x=0.75 (or 1) is presently understood by their possible different scattering mechanism of the anomalous Hall effect due to the differences in atomic order and conductivity. Our work can expand the existing understanding of the SGS properties and offer a better SGS candidate with higher carrier mobility that can facilitate the application in the spin-injected related devices.

References in corpus (12)