Jahn-Teller-driven Phase Segregation in Mn${}_x$Co${}_{3-x}$O${}_4$ Spinel Thin Films

Abstract

Transition metal spinel oxides comprised of Earth-abundant Mn and Co have long been explored for their use in catalytic reactions and energy storage. However, understanding of functional properties can be challenging due to differences in sample preparation and the ultimate structural properties of the materials. Epitaxial thin film synthesis provides a novel means of producing precisely-controlled materials to explore the variations reported in the literature. In this work, Mn${}_x$Co${}_{3-x}$O${}_4$ samples from x = 0 to x = 1.28 were synthesized through molecular beam epitaxy and characterized to develop a material properties map as a function of stoichiometry. Films were characterized via in situ X-ray photoelectron spectroscopy, X-ray diffraction, scanning transmission electron microscopy, and polarized K-edge X-ray absorption spectroscopy. Mn cations within this range were found to be octahedrally coordinated, in line with an inverse spinel structure. Samples largely show mixed Mn${}^{3+}$ and Mn${}^{4+}$ character with evidence of phase segregation tendencies with increasing Mn content and increasing Mn${}^{3+}$ formal charge. Phase segregation may occur due to structural incompatibility between cubic and tetragonal crystal structures associated with Mn${}^{4+}$ and Jahn-Teller active Mn${}^{3+}$ octahedra, respectively. Our results help to explain the reported differences across samples in these promising materials for renewable energy technologies.

arXiv comment25 pages, 8 figures; Supplemental info and figures, 9 pages

References in corpus (6)

• Lattice parameters and stability of the spinel compounds in relation to the ionic radii and electronegativities of constituting chemical elements
• Experimental study of the interfacial cobalt oxide in Co3O4/a-Al2O3(0001) epitaxial films
• Oxygen Reduction Electrocatalysis with Epitaxially Grown Spinel MnFe${}_2$O${}_4$ and Fe${}_3$O${}_4$
• Probing Emergent Surface and Interfacial Properties in Complex Oxides via in situ X-ray Photoelectron Spectroscopy
• Systematic analysis of structural and magnetic properties of spinel $Co{B}_2{O}_4$(B=Cr,Mn and Fe)compounds from their electronic structures
• Growth and characterization of thin epitaxial Co3O4(111) films