The nature of deformation-induced dislocations in SrTiO3: Insights from atomistic simulations
arXiv:2207.13631 · doi:10.1016/j.actamat.2022.118404
Abstract
The nature of mechanically induced dislocations in SrTiO3 at low temperatures has been a disputed matter for a long time. Here we provide a systematic overview of the existing knowledge on dislocations in stoichiometric SrTiO3 complemented by computational models of several of the proposed dislocation types. Based on atomistic simulations we reveal their structure and mobility and put our focus on the splitting into partial dislocations, because this mechanism is held responsible for the good dislocation mobility in strontium titanate. Our results reveal that dislocations with a {1-10} glide plane (types A, B, and C) show easy glide behavior due to their glide dissociated configuration. The motion of dislocations on {001} glide planes (type E), however, is prohibited due to high Peierls barriers, as is the case for the {1-1-2} glide plane (type D). For dislocations with (partial) edge character the dissociation into partials is shown to be very sensitive to the charge state of the dislocation core. Since, in turn, dislocation mobility is strongly related to the dissociation of dislocations, the macroscopic ductility may in some cases have a direct relation to the charge at the dislocation core.
Cited by in corpus (8)
- Harvesting room-temperature plasticity in ceramics by mechanically seeded dislocations
- Damage-tolerant oxides by imprint of an ultra-high dislocation density
- Room-temperature bulk plasticity and tunable dislocation densities in KTaO3
- Room-temperature dislocation plasticity in ceramics: Methods, Materials, and Mechanisms
- Low temperature state in strontium titanate microcrystals using in situ multi-reflection Bragg coherent X-ray diffraction imaging
- Dislocation response to electric fields in strontium titanate: A mesoscale indentation study
- Ferroelectric switching at edge dislocations in BaTiO modelled at the atomic scale
- Oxygen Vacancies at Dislocation Core Modulate Plasticity in Strontium Titanate