Solar cell efficiency, diode factor and interface recombination: insights from photoluminescence

Abstract

Metastable defects can decisively influence the diode factor and thus the efficiency of a solar cell. The diode factor is also influenced by the doping level and the recombination mechanisms in the solar cell. Here we quantify how the various parameters change the diode factor by photoluminescence measurements and simulations. In addition, we show that backside recombination reduces the open circuit voltage in CuInSe2 solar cells by more than 40 mV. Passivation by a Ga gradient is shown to be as efficient as a passivation by dielectric layers. Increased backside recombination reduces the diode factor, not because of less metastable defect transformation but because of a sublinear increase in photo generated carriers with excitation. This reduction in diode factor is unwanted, since the increased recombination reduces the voltage. A higher doping level, on the other hand, reduces the diode factor, thereby increasing the fill factor, and at the same time increases the voltage.

Cited by in corpus (7)

• Composition variations in Cu(In,Ga)(S,Se)2 solar cells: not a gradient, but an interlaced network of two phases
• Improved sequentially processed Cu(In,Ga)(S,Se)2 by Ag alloying
• CuIn(Se,Te)2 absorbers with bandgaps < 1 eV for bottom cells in tandem applications
• The effect of a band gap gradient on the radiative losses in the open circuit voltage of solar cells
• Sodium induced beneficial effects in wide bandgap Cu(In,Ga)S2 solar cell with 15.7% efficiency
• Silver Alloyed Wide Bandgap (Ag,Cu)(In,Ga)S2 Thin Film Solar Cells With 15.5% Efficiency
• Sub-micron Cu(In,Ga)Se2 solar cell with efficiency of 18.2% enabled by a hole transport layer