Modeling crack propagation in heterogeneous materials: Griffith's law, intrinsic crack resistance and avalanches

Abstract

Various kinds of heterogeneity in solids including atomistic discreteness affect the fracture strength as well as the failure dynamics remarkably. Here we study the effects of an initial crack in a discrete model for fracture in heterogeneous materials, known as the fiber bundle model. We find three distinct regimes for fracture dynamics depending on the initial crack size. If the initial crack is smaller than a certain value, it does not affect the rupture dynamics and the critical stress. While for a larger initial crack, the growth of the crack leads to a breakdown of the entire system, and the critical stress depends on the crack size in a power-law manner with a nontrivial exponent. The exponent, as well as the limiting crack size, depend on the strength of heterogeneity and the range of stress relaxation in the system.

arXiv comment12 pages, 6 figures

References in corpus (13)

• The fracture of highly deformable soft materials: A tale of two length scales
• Burst avalanches in solvable models of fibrous materials
• From damage percolation to crack nucleation through finite size criticality
• Fracture model with variable range of interaction
• Fracturing highly disordered materials
• Modes of failures in disordered solids
• Nucleation versus percolation: Scaling criterion for failure in disordered solids
• Onset of Localization in Heterogeneous Interfacial Failure
• The Local load sharing fiber bundle model in higher dimensions
• Spatial scaling in fracture propagation in dilute systems
• Record statistics of bursts signals the onset of acceleration towards failure
• Cracks in random brittle solids: From fiber bundles to continuum mechanics
• Predictability and Strength of a Heterogeneous System : The Role of System Size and Disorder