All Inorganic p_n Heterojunction Solar Cells by Solution Combustion Synthesis using n_type FeMnO3 Perovskite Photoactive Layer
arXiv:2112.08057 · doi:10.3389/fchem.2021.754487
Abstract
This study outlines the synthesis and physicochemical characteristics of a solution-processable iron manganite (FeMnO3) nanoparticles via a chemical combustion method using tartartic acid as a fuel and demonstrates the performance of this material as a n-type photoactive layer in all-oxide solar cells. It is shown that the solution combustion synthesis (SCS) method enables the formation of pure crystal phase FeMnO3 with controllable particle size. XRD pattern and morphology images from TEM confirm the purity of FeMnO3 phase and the relative small crystallite size (~13 nm), firstly reported in the literature. Moreover, to assemble a network of connected FeMnO3 nanoparticles, \b{eta}-alanine was used as a capping agent and dimethylformamide (DMF) as a polar aprotic solvent for the colloidal dispersion of FeMnO3 NPs. This procedure yields a ~500 nm thick photoactive layer. The proposed method is crucial to obtain functional solution processed NiO/FeMnO3 heterojunction inorganic photovoltaics. The optoelectronic properties of the heterojunction were established. These solar cells demonstrate a high open circuit voltage of 1.31 V with sufficient fill factor of 54.3% and low short circuit current of 0.07 mA cm-2 delivering a power conversion efficiency of 0.05% under 100 mW cm-2 illumination. This work expands on the burgeoning of environmentally friendly, low-cost, sustainable solar cell material that derive from metal oxides.
arXiv comment19 pages, 8 figures
References in corpus (6)
- Low Temperature Combustion Synthesis of a Spinel NiCo2O4 Hole Transport Layer for Perovskite Photovoltaics
- The Effect of Hole Transporting Layer in Charge Accumulation Properties of p-i-n Perovskite Solar Cells
- Employing surfactant-assisted hydrothermal synthesis to control CuGaO2 nanoparticle formation and improved carrier selectivity of perovskite solar cells
- Room Temperature Nanoparticulate Interfacial Layers for Perovskite Solar Cells via solvothermal synthesis
- Enhanced Photovoltaic Performance of Perovskite Solar Cells by Co-Doped Spinel Nickel Cobaltite Hole Transporting Layer
- Nanoparticulate Metal Oxide Top Electrode Interface Modification Improves the Thermal Stability of Inverted Perovskite Photovoltaics