Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks

Abstract

The most effective way to enhance the dissipation-free supercurrent in presence of magnetic field for type II superconductors is the introduction of defects that acts as artificial pinning centres (APCs) for the vortices. For instance, the in-field critical current density of doped BaFe2As2 (Ba122), one of the most technologically important Fe-based superconductors, has been improved over the last decade by APCs created by ion-irradiation. The technique of ion-irradiation has been commonly implemented to determine the ultimate superconducting properties. However, this method is rather complicated and expensive. Here, we report on a surprisingly high critical current density and strong pinning efficiency close to the crystallographic c-axis for a K-doped Ba122 epitaxial thin film without APCs, achieving performance comparable to ion-irradiated K-doped Ba122 single crystals. Microstructural analysis reveals that the film is composed of columnar grains having width around 30-60 nm. The grains are rotated around the b- (or a-) axis by 1.5 degree and around the c-axis by -1 degree, resulting in the formation of low-angle grain boundary networks. This study demonstrates that the upper limit of in-field properties reached in ion-irradiated K-doped Ba122 is achievable by grain boundary engineering, which is a simple and industrially scalable manner.

Main text with Supplement Material

References in corpus (6)

• Upper critical fields and thermally-activated transport of Nd(O_0.7F_0.3)FeAs single crystal
• Biaxially textured cobalt-doped BaFe2As2 films with high critical current density over 1 MA/cm2 on MgO-buffered metal-tape flexible substrates
• Doping-dependent critical current properties in K, Co, and P-doped BaFe2As2 single crystals
• Fe-based superconducting thin films on metallic substrates: growth, characteristics and relevant properties
• High-field transport properties of a P-doped BaFe2As2 film on technical substrate
• Realization of epitaxial thin films of the superconductor K-doped BaFe${}_{\text{2}}$As${}_{\text{2}}$

Cited by in corpus (2)

• Strengthened proximity effect at grain boundaries to enhance inter-grain supercurrent in Ba1-xKxFe2As2 superconductors
• K-doped Ba122 epitaxial thin film on MgO substrate by buffer engineering