Growth and Characterization of Fe0.95Se0.6Te0.4 Single Crystal

Abstract

In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are detectable. The stoichiometric composition has been verified by energy dispersive x-ray analysis. The superconducting transition temperature at 14 K was confirmed through DC magnetization (ZFC-FC) and resistivity measurements. By analyzing the isothermal M-H curves, we determined the value of H_c1 (0) ~360 Oe by extrapolating the data. The temperature coefficient of resistivity obtained using the power law fitting was found to be 0.6. The obtained Raman spectra at room temperature can be interpreted with the tetragonal crystal structure and space group P4/nmm.

conference paper

References in corpus (5)

• Tellurium substitution effect on superconductivity of the alpha-phase Iron Selenide
• Bulk Superconductivity at 14 K in Single Crystals of Fe1+yTexSe1-x
• Substitution Effects on FeSe Superconductor
• Anomalous Raman scattering from phonons and electrons of superconducting FeSe${}_{0.82}$
• Phonon, Two-Magnon and Electronic Raman Scattering of Fe1+yTe1-xSex