Cluster superconductivity in the magnetoelectric Pb(Fe1/2Sb1/2)O3 ceramics

Abstract

We report the observation of cluster (local) superconductivity in the magnetoelectric Pb(Fe1/2Sb1/2)O3 ceramics prepared at a hydrostatic pressure of 6 GPa and temperatures 1200-1800 K to stabilize the perovskite phase. The superconductivity is manifested by an abrupt drop of the magnetic susceptibility at the critical temperature TC 7 K. Both the magnitude of this drop and TC decrease with magnetic field increase. Similarly, the low-field paramagnetic absorption measured by EPR spectrometer drops significantly below TC as well. The observed effects and their critical magnetic field dependence are interpreted as manifestation of the superconductivity and Meissner effect in metallic Pb nanoclusters existing in the ceramics. Their volume fraction and average size were estimated as 0.1-0.2% and 140-150 nm, respectively. The superconductivity related effects disappear after oxidizing annealing of the ceramics.

arXiv comment9 pages, 5 figures

References in corpus (10)

• Direct imaging of the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 interface
• Coexistence of Magnetic Order and Two-dimensional Superconductivity at LaAlO${}_3$/SrTiO${}_3$ Interfaces
• Theory of the SrTiO3 Surface State Two-Dimensional Electron Gas
• Microscopic Coexistence of Antiferromagnetic and Spin-Glass States
• Spin-glass state and long-range magnetic order in Pb(Fe1/2Nb1/2)O3
• Room-temperature paramagnetoelectric effect in magnetoelectric multiferroics Pb(Fe1/2Nb1/2)O3 and its solid solution with PbTiO3
• Magnetic interactions in disordered perovskite PbFe_{1/2}Nb_{1/2}O_3 and related compounds. Dominance of nearest-neighbor interaction
• Macroscopic description of the two-dimensional LaAlO${}_3$/SrTiO${}_3$ interface
• Transversal spin freezing and re-entrant spin glass phase in chemically disordered Fe-contained double perovskite multiferroics
• Two-dimensional electron gas at the LaAlO${}_3$/SrTiO${}_3$ inteface with a potential barrier