La1-xBi1+xS3 (x~0.08): An n-Type Semiconductor

Abstract

The new bismuth chalcogenide La0.92Bi1.08S3 crystallizes in the monoclinic space group C2/m with a = 28.0447(19) Å, b = 4.0722(2) Å, c = 14.7350(9) Å, and $\beta$ = 118.493(5)°. The structure of La0.92Bi1.08S3 is built up of NaCl-type Bi2S5 blocks, and BiS4 and LaS5 infinitely long chains forming a compact three-dimensional framework with parallel tunnels. Optical spectroscopy and resistivity measurements reveal a semiconducting behavior with a band gap of ~ 1 eV and activation energy for transport of 0.36(1) eV. Thermopower measurements suggest the majority carriers of La0.92Bi1.08S3 are electrons. Heat capacity measurements indicate no phase transitions from 2 to 300 K. Band structure calculations at the density functional theory level confirm the semiconducting nature and the indirect gap of La0.92Bi1.08S3.

References in corpus (7)

• Discovery (theoretical prediction and experimental observation) of a large-gap topological-insulator class with spin-polarized single-Dirac-cone on the surface
• High-temperature superconductivity in iron-based materials
• Superconductivity in CuxBi2Se3 and its implications for pairing in the undoped topological insulator
• Superconductivity in novel BiS2-based layered superconductor LaO1-xFxBiS2
• Superconductivity Appears in the Vicinity of an Insulating-Like Behavior in CeO${}_{1-x}$F${}_x$BiS${}_2$
• Manipulation of Topological States and Bulk Band Gap Using Natural Heterostructures of a Topological Insulator
• Dirac Fermions and Superconductivity in Homologous Structures (AgxPb1-xSe)5(Bi2Se3)3m,m = 1,2