Suppression of magnetoresistance in thin $WT{e}_2$ flakes by surface oxidation

Abstract

Recent renewed interest in layered transition metal dichalcogenides stems from the exotic electronic phases predicted and observed in the single- and few-layer limit. Realizing these electronic phases requires preserving the desired transport properties down to a monolayer, which is challenging. Here, using semimetallic $WT{e}_2$ that exhibits large magnetoresistance, we show that surface oxidation and Fermi level pinning degrade the transport properties of thin $WT{e}_2$ flakes significantly. With decreasing $WT{e}_2$ flake thickness, we observe a dramatic suppression of the large magnetoresistance. This is explained by fitting a two-band model to the transport data, which shows that mobility of the electron and hole carriers decreases significantly for thin flakes. The microscopic origin of this mobility decrease is attributed to a ~ 2 nm-thick amorphous surface oxide layer that introduces disorder. The oxide layer also shifts the Fermi level by ~ 300 meV at the $WT{e}_2$ surface. However, band bending due to this Fermi level shift is not the dominant cause for the suppression of magnetoresistance as the electron and hole carrier densities are balanced down to ~ 13 nm based on the two-band model. Our study highlights the critical need to investigate often unanticipated and sometimes unavoidable extrinsic surface effects on the transport properties of layered dichalcogenides and other 2D materials.

arXiv comment4 Figures

References in corpus (1)

• The Effect of Dopants on the Magnetoresistance of WTe2

Cited by in corpus (5)

• Direct evidence for charge compensation induced large magnetoresistance in thin WTe2
• Thickness dependent electronic structure in WTe${}_2$ thin films
• Crossover Between Weak Antilocalization and Weak Localization and Electron-Electron Interaction in Few-Layer WTe${}_2$
• Thickness Dependence of Magneto-transport Properties in Tungsten Ditelluride
• Temperature effect on lattice and electronic structures of WTe${}_2$ from first-principles study