Elastic and Piezoresistive Properties of Nickel Carbides from First-Principles

Abstract

The nickel--carbon system has received increased attention over the past years due to the relevance of nickel as a catalyst for carbon nanotube and graphene growth, where Nickel carbide intermediates may be involved or carbide interface layers form in the end. Nickel--carbon composite thin films comprising Ni${}_3$C are especially interesting in mechanical sensing applications. Due to the meta-stability of nickel carbides, formation conditions and the coupling between mechanical and electrical properties are not yet well understood. Using first-principles electronic structure methods, we calculated the elastic properties of Ni${}_3$C, Ni${}_2$C and NiC, as well as changes in electronic properties under mechanical strain. We observe that the electronic density of states around the Fermi level does not change under the considered strains of up to 1%, which correspond to stresses up to 3GPa. Relative changes in conductivity of Ni${}_3$C range up to maximum values of about 10%.

Accepted for publication in Phys. Rev B

References in corpus (5)

• Electronic structure and transport anisotropy of Bi2Te3 and Sb2Te3
• Crystallization characteristics and chemical bonding properties of nickel carbide thin film nanocomposites
• Ni/Ni3C Core-Shell Nanochains and Its Magnetic Properties: One-Step Synthesis at low temperature
• DFT investigations of the piezoresistive effect of carbon nanotubes for sensor application
• Empirical transport model of strained CNT transistors used for sensor applications