Step bunching and macrostep formation in 1D atomistic scale model of unstable vicinal crystal growth
arXiv:1601.07371 · doi:10.1016/j.jcrysgro.2016.11.121
Abstract
We devise a new 1D atomistic scale model of vicinal growth based on Cellular Automaton. In it the step motion is realized by executing the automaton rule prescribing how adatoms incorporate into the vicinal crystal. Time increases after each rule execution and then nDS diffusional updates of the adatoms are performed. The increase of nDS switches between the diffusion-limited (DL, nDS=1) and kinetics-limited (KL, nDS >> 1) regimes of growth. We study the unstable step motion by employing two alternative sources of instability - biased diffusion and infinite inverse Ehrlich-Schwoebel barrier (iiSE). The resulting step bunches consist of steps but also of macrosteps since there is no step-step repulsion incorporated explicitly into the model. This complex pattern formation is quantified by studying the time evolution of the bunch size N and macrostep size Nm in order to find the proper parameter combinations that rescale the time and thus to obtain the full time-scaling relations including the pre-factors. For the case of biased diffusion the time-scaling exponent beta of N is 1/2 while for the case of iiSE it is 1/3. In both cases the time-scaling exponent beta_m of Nm is ~3beta/4 in the DL regime and 3beta/5 in the KL one.
9 pages, 9 figures
References in corpus (4)
Cited by in corpus (8)
- Step bunching with both directions of the current: Vicinal W(110) surfaces versus atomistic scale model
- Diffusion-Dependent Pattern Formation on Crystal Surfaces
- Step meandering: The balance between the potential well and the Ehrlich-Schwoebel barrier
- Scaling laws for step bunching on vicinal surfaces: the role of the dynamical and chemical effects
- Surface Patterns Shaped by Additives in Crystals
- Engineering 2D Surface Patterns with the VicCa Model
- Bunch width versus macrostep height: A quantitative study of the effects of step-step repulsion
- Relationship Between Macrostep Height and Surface Velocity for a Reaction-Limited Crystal Growth Process