Molecular Beam Epitaxy Growth of Superconducting LiFeAs Film on SrTiO3(001) Substrate
arXiv:1503.03216 · doi:10.1209/0295-5075/109/28003
Abstract
The stoichiometric "111" iron-based superconductor, LiFeAs, has attacted great research interest in recent years. For the first time, we have successfully grown LiFeAs thin film by molecular beam epitaxy (MBE) on SrTiO3(001) substrate, and studied the interfacial growth behavior by reflection high energy electron diffraction (RHEED) and low-temperature scanning tunneling microscope (LT-STM). The effects of substrate temperature and Li/Fe flux ratio were investigated. Uniform LiFeAs film as thin as 3 quintuple-layer (QL) is formed. Superconducting gap appears in LiFeAs films thicker than 4 QL at 4.7 K. When the film is thicker than 13 QL, the superconducting gap determined by the distance between coherence peaks is about 7 meV, close to the value of bulk material. The ex situ transport measurement of thick LiFeAs film shows a sharp superconducting transition around 16 K. The upper critical field, Hc2(0)=13.0 T, is estimated from the temperature dependent magnetoresistance. The precise thickness and quality control of LiFeAs film paves the road of growing similar ultrathin iron arsenide films.
7 pages, 6 figures
References in corpus (9)
- The superconductivity at 18 K in LiFeAs system
- LiFeAs: An Intrinsic FeAs-based Superconductor with Tc = 18K
- Structure and superconductivity of LiFeAs
- Anisotropic Energy Gaps of Iron-based Superconductivity from Intra-band Quasiparticle Interference in LiFeAs
- Scanning Tunneling Microscopy/Spectroscopy of Vortices in LiFeAs
- Scanning tunneling spectroscopy of superconducting LiFeAs single crystals: Evidence for two nodeless energy gaps and coupling to a bosonic mode
- Theory for Magnetism and Triplet Superconductivity in LiFeAs
- Synthesis, anisotropy, and superconducting properties of LiFeAs single crystal
- Pressure shift of the superconducting T_c of LiFeAs