Persistent semi-metal-like nature of epitaxial perovskite CaIrO3 thin films

Abstract

Strong spin-orbit coupled 5d transition metal based ABO3 oxides, especially iridates, allow tuning parameters in the phase diagram and may demonstrate important functionalities, for example, by means of strain effects and symmetry-breaking, because of the interplay between the Coulomb interactions and strong spin-orbit coupling. Here, we have epitaxially stabilized high quality thin films of perovskite (Pv) CaIrO3. Film on the best lattice-matched substrate shows semi-metal-like characteristics. Intriguingly, imposing tensile or compressive strain on the film by altering the underlying lattice-mismatched substrates still maintains semi-metallicity with minute modification of the effective correlation as tensile (compressive) strain results in tiny increases (decreases) of the electronic bandwidth. In addition, magnetoresistance remains positive with a quadratic field dependence. This persistent semi-metal-like nature of Pv-CaIrO3 thin films with minute changes in the effective correlation by strain may provide new wisdom into strong spin-orbit coupled 5d based oxide physics.

Published in Journal of Applied Physics

References in corpus (7)

• Novel Jeff = 1/2 Mott State Induced by Relativistic Spin-Orbit Coupling in Sr2IrO4
• Bandwidth-Controlled Insulator-Metal Transition and Correlated Metallic State in 5$d$ Transition Metal Oxides Sr${}_{n+1}$Ir${}_n$O${}_{3n+1}$ ($n$=1, 2, and $\infty$)
• Interplay of Spin-Orbit Interactions, Dimensionality, and Octahedral Rotations in Semimetallic SrIrO${}_3$
• Compressive strain-induced metal-insulator transition in orthorhombic SrIrO3 thin films
• Tunable Semimetallic State in Compressive-strained SrIrO3 Films Revealed by Transport Behaviors
• CaIrO3 post-perovskite, a j = 1/2 quasi-one-dimensional antiferromagnet
• Effects of substrate temperature on the unusual non-Fermi liquid metal to insulator transition in perovskite SrIrO3 thin films

Cited by in corpus (1)

• Magnetism tailored by mechanical strain engineering in PrVO${}_3$ thin films