Comparative study of the effects of electron irradiation and natural disorder in single crystals of SrFe${}_2$(As${}_{1-x}$P${}_x$)${}_2$ ($x=$0.35) superconductor

Abstract

London penetration depth, $\lambda (T)$, was measured in single crystals of SrFe${}_2$(As${}_{1-x}$P${}_x$)${}_2$ ($x=$0.35) iron - based superconductor. The influence of disorder on the transition temperature, $T_c$, and on $\lambda (T)$ was investigated. The effects of scattering controlled by the annealing of as-grown crystals was compared with the effects of artificial disorder introduced by 2.5~MeV electron irradiation. The low temperature behavior of $\lambda (T)$ can be described by a power-law function, $\Delta \lambda (T)=A{T}^n$, with the exponent $n$ close to one in pristine annealed samples, as expected for superconducting gap with line nodes. Upon $1.2\times 10^{19}$ \ecm irradiation, the exponent $n$ increases rapidly exceeding a dirty limit value of $n=$ 2 implying that the nodes in the superconducting gap are accidental and can be lifted by the disorder. The variation of the exponent $n$ with $T_c$ is much stronger in the irradiated crystals compared to the crystals in which disorder was controlled by the annealing of the growth defects. We discuss the results in terms of different influence of different types of disorder on intra- and inter- band scattering.

References in corpus (5)

• Magnetic Penetration Depth in Unconventional Superconductors
• A Sharp Peak of the Zero-Temperature Penetration Depth at Optimal Composition in BaFe2(As1-xPx)2
• Microwave Surface-Impedance Measurements of the Magnetic Penetration Depth in Single Crystal Ba1-xKxFe2As2 Superconductors: Evidence for a Disorder-Dependent Superfluid Density
• Magneto-optical study of Ba(Fe${}_{1-x}$T${}_x$)${}_2$As${}_2$ (T=Co, Ni) single crystals irradiated with heavy-ions
• Investigation of the Superconducting Gap Structure in SrFe${}_2$(As${}_{0.7}$P${}_{0.3}$)${}_2$ by Magnetic Penetration Depth and Flux Flow Resistivity Analysis

Cited by in corpus (2)

• Effects of electron irradiation on resistivity and London penetration depth of Ba${}_{1-x}$K${}_x$Fe${}_2$As${}_2$ ($x\le$ 0.34) iron - pnictide superconductor
• Effect of disorder on the competition between nematic and superconducting order in FeSe