Displacement cascades and defects annealing in tungsten, Part I: defect database from molecular dynamics simulations

Abstract

Molecular dynamics simulations have been used to generate a comprehensive database of surviving defects due to displacement cascades in bulk tungsten. Twenty one data points of primary knock-on atom (PKA) energies ranging from 100 eV (sub-threshold energy) to 100 keV ($\sim$780$\times E_d$, where $E_d$ is the average displacement threshold energy) have been completed at 300 K, 1025 K and 2050 K. Within this range of PKA energies, two regimes of power-law energy-dependence of the defect production are observed. A distinct power-law exponent characterizes the number of Frenkel pairs produced within each regime. The two regimes intersect at a transition energy which occurs at approximately 250$\times E_d$. The transition energy also marks the onset of the formation of large self-interstitial atom (SIAs) clusters (size 14 or more). The observed defect clustering behavior is asymmetric, with SIA clustering increasing with temperature, while the vacancy clustering decreases. This asymmetry increases with temperature such that at 2050 K ($\sim 0.5T_m$) practically no large vacancy clusters are formed, meanwhile large SIA clusters appear in all simulations. The implication of such asymmetry on the long-term defect survival and damage accumulation is discussed. In addition, rare $<$100$>${110} SIA loops are observed.

arXiv comment10 pages, 6 figures

References in corpus (1)

• Displacement cascades and defects annealing in tungsten, Part II: Object kinetic Monte Carlo Simulation of Tungsten Cascade Aging

Cited by in corpus (9)

• Mechanism of Re precipitation in irradiated W-Re alloys from kinetic Monte Carlo simulations
• Atomistic-Object Kinetic Monte Carlo simulations of irradiation damage in tungsten
• Graph Theory Based Approach to Characterize Self Interstitial Defect Morphology
• Controlled irradiation hardening of tungsten by cyclic recrystallization
• Comparison of SIA Defect Morphologies from Different Interatomic Potentials for Collision Cascades in W
• On the detection and classification of material defects in crystalline solids after energetic particle impact simulations
• Compressing and forecasting atomic material simulations with descriptors
• Outstanding Radiation Resistance of Tungsten-based High Entropy Alloys
• Long-term microstructural evolution of tungsten under heat and neutron loads