Persistent metal-insulator transition at the surface of an oxygen-deficient, epitaxial manganite film

Abstract

The oxygen stoichiometry has a large influence on the physical and chemical properties of complex oxides. Most of the functionality in e.g. catalysis and electrochemistry depends in particular on control of the oxygen stoichiometry. In order to understand the fundamental properties of intrinsic surfaces of oxygen-deficient complex oxides, we report on in situ temperature dependent scanning tunnelling spectroscopy experiments on pristine oxygen deficient, epitaxial manganite films. Although these films are insulating in subsequent ex situ in-plane electronic transport experiments at all temperatures, in situ scanning tunnelling spectroscopic data reveal that the surface of these films exhibits a metal-insulator transition (MIT) at 120 K, coincident with the onset of ferromagnetic ordering of small clusters in the bulk of the oxygen-deficient film. The surprising proximity of the surface MIT transition temperature of nonstoichiometric films with that of the fully oxygenated bulk suggests that the electronic properties in the surface region are not significantly affected by oxygen deficiency in the bulk. This carries important implications for the understanding and functional design of complex oxides and their interfaces with specific electronic properties for catalysis, oxide electronics and electrochemistry.

References in corpus (8)

• Magnetic effects at the interface between nonmagnetic oxides
• Strain controlled oxygen vacancy formation and ordering in CaMnO${}_3$
• Quantum many-body interactions in digital oxide superlattices
• Suppressed Magnetization at the Surfaces and Interfaces of Ferromagnetic Metallic Manganites
• Highly anisotropic resistivities in the double-exchange model for strained manganites
• Manifestations of Broken Symmetry: The Surface Phases of Ca(2-x)Sr(x)RuO4
• Tunneling Study of the Charge-Ordering Gap on the Surface of La${}_{0.350}$Pr${}_{0.275}$Ca${}_{0.375}$MnO${}_3$ Thin Films
• Interplay between strain and oxygen vacancies in lanthanum aluminate