Specific Heat Discontinuity DeltaC vs Tc in Annealed Ba(Fe1-xCox)2As2

Abstract

The low temperature specific heat of annealed single crystal samples of Ba(Fe1-xCox)2As2 with compositions spanning the entire superconducting phase diagram was measured. Effort was made to discover the best annealing schedule to maximize Tc and minimize transition width in these samples. Values of deltaC/Tc normalized to 100% superconducting volume fractions varied proportionally to Tc^alpha. Within a rather narrow error bar of +-0.15, the exponent alpha was the same (approximately 2) over a range of compositions (0.055 < x < 0.15) around the optimal concentration, x=0.08, where Tc is the maximum in the phase diagram. Thus, whether the superconductivity was coexistent with magnetism (underdoped) or not (overdoped) did not affect the non-BCS variation (alpha nearly 2 instead of 0.8-0.9 for BCS superconductors) of deltaC/Tc with Tc. The annealed samples in the present work, with increased deltaC/Tc and Tc values compared to previous results for the Ba(Fe1-xCox)2As2 alloy system, suggest that the intrinsic value of the exponent alpha for the iron superconductors, when the samples are annealed, with fewer defects, may indeed be even further from the BCS value of 0.8-0.9 than previously thought.

References in corpus (8)

• Scanning tunneling spectroscopy of high-temperature superconductors
• Fully Gapped Superconducting State Based on a High Normal State Quasiparticle Density of States in Ba${}_{0.6}$K${}_{0.4}$Fe${}_2$As${}_2$ Single Crystals
• Low temperature specific heat of the hole-doped Ba_{0.6}K_{0.4}Fe_2As_2 single crystals and electron-doped SmFeAsO_{0.9}F_{0.1} samples
• A doping dependent specific heat study of the superconducting gap in Ba(Fe${}_{1-x}$Co${}_x$)${}_2$As${}_2$
• Effect of annealing on the specific heat of Ba(Fe1-xCox)2As2
• Specific Heat Discontinuity, deltaC, at Tc in BaFe2(As0.7P0.3)2 - Consistent with Unconventional Superconductivity
• Specific Heat To Hc2: Evidence for Nodes or Deep Minima in the Superconducting Gap of Under- and Overdoped Ba(Fe1-xCox)2As2
• Effect of annealing on the specific heat of optimally doped Ba(Fe${}_{0.92}$Co${}_{0.08}$)${}_2$As${}_2$

Cited by in corpus (5)

• Strong Correlations, Strong Coupling and s-wave Superconductivity in Hole-doped BaFe2As2 Single Crystals
• Temperature-concentration phase diagram of (Ca1-xLax)10(Pt3As8)(Fe2As2)5 superconductors
• Evolution of London penetration depth with scattering in single crystals of K${}_{1-x}$Na${}_x$Fe${}_2$As${}_2$
• Unusual Sensitivity of Superconductivity to Strain in Iron-Based 122 Superconductors
• Superconductivity In K- And Na- Doped Bafe2as2: What Can We Learn From Heat Capacity And Pressure Dependence of Tc