The Role of Interdiffusion and Spatial Confinement in the Formation of Resonant Raman Spectra of Ge/Si(100) Heterostructures with Quantum-Dot Arrays

Abstract

The phonon modes of self-assembled Ge/Si quantum dots grown by molecular-beam epitaxy in an apparatus integrated with a chamber of the scanning tunneling microscope into a single high-vacuum system are investigated using Raman spectroscopy. It is revealed that the Ge-Ge and Si-Ge vibrational modes are considerably enhanced upon excitation of excitons between the valence band ${\Lambda }_3$ and the conduction band ${\Lambda }_1$ (the E1 and E1 + ${\Delta }_1$ transitions). This makes it possible to observe the Raman spectrum of very small amounts of germanium, such as one layer of quantum dots with a germanium layer thickness of 10 Å. The enhancement of these modes suggests a strong electron-phonon interaction of the vibrational modes with the E1 and E1 + ${\Delta }_1$ excitons in the quantum dot. It is demonstrated that the frequency of the Ge-Ge mode decreases by 10 cm^-1 with a decrease in the thickness of the Ge layer from 10 to 6 Å due to the spatial-confinement effect. The optimum thickness of the Ge layer, for which the size dispersion of quantum dots is minimum, is determined.

arXiv comment14 pages, 9 figures

Cited by in corpus (5)

• CMOS compatible dense arrays of Ge quantum dots on the Si(001) surface: Hut cluster nucleation, atomic structure, and array life cycle during UHV MBE growth
• Ge quantum dot arrays grown by ultrahigh vacuum molecular beam epitaxy on the Si(001) surface: nucleation, morphology and CMOS compatibility
• Ge/Si(001) heterostructures with dense arrays of Ge quantum dots: morphology, defects, photo-emf spectra and terahertz conductivity
• The formation of intermediate layers in covered Ge/Si heterostructures with low-temperature quantum dots: a study using high-resolution transmission electron microscopy and Raman spectroscopy
• Classification of Ge hut clusters in the arrays formed by molecular beam epitaxy at low temperatures on the Si(001) surface