Calculating the trap density of states in organic field-effect transistors from experiment: A comparison of different methods

Abstract

The spectral density of localized states in the band gap of pentacene (trap DOS) was determined with a pentacene-based thin-film transistor from measurements of the temperature dependence and gate-voltage dependence of the contact-corrected field-effect conductivity. Several analytical methods to calculate the trap DOS from the measured data were used to clarify, if the different methods lead to comparable results. We also used computer simulations to further test the results from the analytical methods. Most methods predict a trap DOS close to the valence band edge that can be very well approximated by a single exponential function with a slope in the range of 50-60 meV and a trap density at the valence band edge of approx. 2x10E21 eV-1cm-3. Interestingly, the trap DOS is always slightly steeper than exponential. An important finding is that the choice of the method to calculate the trap DOS from the measured data can have a considerable effect on the final result. We identify two specific simplifying assumptions that lead to significant errors in the trap DOS. The temperature-dependence of the band mobility should generally not be neglected. Moreover, the assumption of a constant effective accumulation layer thickness leads to a significant underestimation of the slope of the trap DOS.

14 pages, 7 figures

References in corpus (1)

• Low-voltage organic transistors and inverters with ultra-thin fluoropolymer gate dielectric

Cited by in corpus (9)

• The trap DOS in small molecule organic semiconductors: A quantitative comparison of thin-film transistors with single crystals
• Structural origin of gap states in semicrystalline polymers and the implications for charge transport
• Shining Light on Photoluminescence Properties of Metal Halide Perovskites
• Approaching the Trap-Free Limit in Organic Single Crystal Field-Effect Transistors
• Gate Bias Stress in Pentacene Field-Effect-Transistors: Charge Trapping in the Dielectric or Semiconductor
• Charge Transport in and Electroluminescence from sp${}^3$-Functionalized Carbon Nanotube Networks
• Spectral, optical and transport properties of the adiabatic anisotropic Holstein model: Application to slightly doped organic semiconductors
• Impact of Dielectric Environment on Trion Emission from Single-Walled Carbon Nanotube Networks
• Analytical Model for Gaussian Disorder Traps in Organic Thin-Film Transistor