Origin of the reduced exchange bias in epitaxial FeNi(111)/CoO(111) bilayer
arXiv:0808.0335 · doi:10.1103/PhysRevB.79.184425
Abstract
We have employed Soft and Hard X-ray Resonant Magnetic Scattering and Polarised Neutron Diffraction to study the magnetic interface and the bulk antiferromagnetic domain state of the archetypal epitaxial NiFe(111)/CoO(111) exchange biased bilayer. The combination of these scattering tools provides unprecedented detailed insights into the still incomplete understanding of some key manifestations of the exchange bias effect. We show that the several orders of magnitude difference between the expected and measured value of exchange bias field is caused by an almost anisotropic in-plane orientation of antiferromagnetic domains. Irreversible changes of their configuration lead to a training effect. This is directly seen as a change in the magnetic half order Bragg peaks after magnetization reversal. A 30 nm size of antiferromagnetic domains is extracted from the width the (1/2 1/2 1/2) antiferromagnetic magnetic peak measured both by neutron and x-ray scattering. A reduced blocking temperature as compared to the measured antiferromagnetic ordering temperature clearly corresponds to the blocking of antiferromagnetic domains. Moreover, an excellent correlation between the size of the antiferromagnetic domains, exchange bias field and frozen-in spin ratio is found, providing a comprehensive understanding of the origin of exchange bias in epitaxial systems.
8 pages, 5 figures, submitted
References in corpus (10)
- Mechanisms of exchange bias with multiferroic BiFeO3 epitaxial thin films
- Positive and Perpendicular Exchange Bias CoO/Co Bilayers
- Exchange bias effect of ferro-/antiferromagnetic heterostructures
- Domain State Model for Exchange Bias
- Origin of asymmetric reversal modes in ferromagnetic/antiferromagnetic multilayers
- Reversing the training effect in exchange biased CoO/Co bilayers
- Quantitative description of the azimuthal dependence of the exchange bias effect
- Ferromagnetic Domain Distribution in Thin Films During Magnetization Reversal
- Modeling exchange bias microscopically
- Soft X-ray Resonant Magnetic Scattering Studies on Fe/CoO Exchange Bias System