Room-temperature ferrimagnetism of anti-site-disordered Ca2MnOsO6
Hai L. Feng, Madhav Prasad Ghimire, Zhiwei Hu +18
Room-temperature ferrimagnetism was discovered for the anti-site-disordered perovskite Ca2MnOsO6 with Tc = 305 K. Ca2MnOsO6 crystallizes into an orthorhombic structure with a space…
Ba2NiOsO6: A Dirac-Mott insulator with ferromagnetism near 100 K
Hai L. Feng, Stuart Calder, Madhav Prasad Ghimire +14
The ferromagnetic semiconductor Ba2NiOsO6 (Tmag ~100 K) was synthesized at 6 GPa and 1500 °C. It crystallizes into a double perovskite structure [Fm-3m; a = 8.0428(1) Å], where the…
Sr3Co2O6: a possible frustrated spin-chain material
X. X. Wang, J. J. Li, Y. G. Shi +9
A dense phase of a post-layered perovskite Sr3Co2O6 was created by a high-pressure and high-temperature synthetic route and quenched to ambient conditions. The structure of Sr3Co2O…
Large decrease in the critical temperature of superconducting LaFeAsO0.85 compounds doped with 3% atomic weight of nonmagnetic Zn impurities
Y. F. Guo, Y. G. Shi, S. Yu +10
We observed a large decrease of Tc by no more than 3 at.% of Zn doped to the optimized superconductor LaFeAsO0.85 (Tc = 26 K), confirmed by measurements of electrical resistivity,…
Superconducting properties of the oxygen-vacant iron oxyarsenide TbFeAsO1-x from underdoped to overdoped compositions
Y. G. Shi, S. Yu, A. A. Belik +8
A wide-range doping was achieved by a high-pressure method for TbFeAsO1-x from "under doped" to "over doped" superconducting compositions throughout the optimized superconductivity…