2 papers
cond-mat.mtrl-sci2026
A Correction Method for Crack Area Overestimation in Phase-Field Fracture
M. Castillón, J. Segurado, I. Romero
Phase-field fracture models are known to overestimate the crack area, a discrepancy that compromises the accuracy of fracture predictions. This issue stems from the diffuse crack r…
cond-mat.mtrl-sci2024
An FFT based chemo-mechanical framework with fracture: application to mesoscopic electrode degradation
Gabriel Zarzoso, Eduardo Roque, Francisco Montero-Chacón +1
An FFT based method is proposed to simulate chemo-mechanical problems at the microscale including fracture, specially suited to predict crack formation during the intercalation pro…