Y. Tsuchiya

most citedSynthesis of CaKFe

_{4}

_{4}

bulk samples with high critical current density using a spark plasma sintering technique

27 citations · 32 across the 3 of their papers we have counts for

collaborators

3 papers

cond-mat.supr-con2026

Superconductivity on the verge of metal-insulator transition in Cu $_{1 - x}$ Zn $_{x}$ Ir $_{2}$ S $_{4}$ probed by $μ$ SR

K. M. Kojima, M. Miyazaki, M. Hiraishi +6

The thiospinel CuIr $_{2}$ S $_{4}$ undergoes a metal-insulator transition below $\approx$ 230 K, which is suppressed by substitution of Cu with Zn (Cu $_{1 - x}$ Zn $_{x}$ Ir $_{2}$ S $_{4}$ ) to induce…

cond-mat.supr-con2024★ 5 cited

Synthesis of $c$ -axis textured CaKFe $_{4}$ As $_{4}$ superconducting bulk via spark plasma texturing technique

Shigeyuki Ishida, Yoshihisa Kamiya, Yoshinori Tsuchiya +7

Grain alignment is a key factor that determines the performance of a superconducting bulk. In this study, the spark plasma texturing (SPT) technique was used to fabricate a CaKFe$_…

cond-mat.supr-con2024★ 27 cited

Synthesis of CaKFe $_{4}$ As $_{4}$ bulk samples with high critical current density using a spark plasma sintering technique

Shigeyuki Ishida, S. Pavan Kumar Naik, Yoshinori Tsuchiya +7

A high density CaKFe $_{4}$ As $_{4}$ bulk sample was successfully synthesized using a spark plasma sintering (SPS) technique. The density of the synthesized sample was 5.02 g cm $^{- 3}$ ,…

Superconductivity on the verge of metal-insulator transition in Cu1−x​Znx​Ir2​S4​ probed by μSR

Synthesis of c-axis textured CaKFe4​As4​ superconducting bulk via spark plasma texturing technique

Synthesis of CaKFe4​As4​ bulk samples with high critical current density using a spark plasma sintering technique

Superconductivity on the verge of metal-insulator transition in Cu $_{1 - x}$ Zn $_{x}$ Ir $_{2}$ S $_{4}$ probed by $μ$ SR

Synthesis of $c$ -axis textured CaKFe $_{4}$ As $_{4}$ superconducting bulk via spark plasma texturing technique

Synthesis of CaKFe $_{4}$ As $_{4}$ bulk samples with high critical current density using a spark plasma sintering technique