Coexistence of superconductivity and sliding polar metal state in HgPSe3
Xiaohui Yu, Wei Zhong, Saori Kawaguchi +8
The simultaneous presence of polarity and metallicity in a material signifies an exotic polar metal state, but such materials are extremely rare, especially in bulk form, due to mu…
Enhancement of Transition Temperature in FexSe0.5Te0.5 Film via Iron Vacancies
J. C. Zhuang, W. K. Yeoh, X. Y. Cui +6
The effects of iron deficiency in FexSe0.5Te0.5 thin films (0.8<x<1) on superconductivity and electronic properties have been studied. A significant enhancement of the superconduct…
On the roles of graphene oxide doping for enhanced supercurrent in MgB2 based superconductors
W. K. Yeoh, X. Y. Cui, B. Gault +13
Due to their graphene-like properties after oxygen reduction, incorporation of graphene oxide (GO) sheets into correlated-electron materials offers a new pathway for tailoring thei…
Graphene doping to enhance flux pinning and supercurrent carrying ability in magnesium diboride superconductor
X. Xu, S. X. Dou, X. L. Wang +6
It has been shown that graphene doping is sufficient to lead to an improvement in the critical current density - field performance (Jc(B)), with little change in the transition tem…
Unconventional superconductivity of NdFeAsO0.82F0.18 indicated by the low temperature dependence of the lower critical field Hc1
X. L. Wang, S. X. Dou, Zhi-An Ren +4
We measured the initial M-H curves for a sample of the newly discovered superconductor NdFeAsO0.82Fe0.18, which had a critical temperature, Tc, of 51 K, and was fabricated at the h…
Effect of nano-carbon particle doping on the flux pinning properties of MgB2 superconductor
S. Soltanian, J. Horvat, X. L. Wang +2
Polycrystalline MgB2-xCx samples with x=0.05, 0.1, 0.2, 0.3, 0.4 nano-particle carbon powder were prepared using an in-situ reaction method under well controlled conditions to limi…