Orientation-selective microwave heating of laser-graphitized diamond at 2.45 GHz
Massimiliano Zamengo, Meguya Ryu, Haoran Mu +6
Pristine diamond couples negligibly to a 2.45 GHz field. We show that femtosecond-laser inscription of a buried graphitic (sp2) architecture makes a 4 x 4 x 2 mm^3 N-doped (100 ppm…
Heating of black-Si by microwaves at 2.45 GHz: effect of nano-needle orientation
Massimiliano Zamengo, Haoran Mu, Hsin-Hui Huang +4
Silicon, which is highly reflective and has negligible absorption at the microwave 2.45 GHz range, can be heated when it is turned into black-Si with a surface texture of nano-need…
Oxidation of Tantalum Nano-Film by Microwave Exposure
Massimiliano Zamengo, Lina Grineviciute, Hsin-Hui Huang +4
Oxidation and ablation of 200 nm tantalum films were carried out by three routes: (i) femtosecond (fs-)laser direct write, (ii) high-temperature annealing (HTA) in a tube furnace,…
Diamond membranes: platform for photonic and opto-mechanical applications
Hsin-Hui Huang, Gediminas Seniutinas, Haoran Mu +8
Diamond 1 - 10 micrometers thick membranes are platform for photonic, quantum and opto-mechanic devices with applications across UV-IR spectral ranges. IR characterization of diamo…
Olivine annealed up to 1500 C: changes traced by polarised IR reflectance and magnetization
Daniel Smith, Donatas Narbutis, Hsin-Hui Huang +14
Spectral analysis at the infrared (IR) spectral range is introduced with assignment of synthetic red-green-blue (RGB) colours defined by adjustable wavelength and bandwidth. The RG…
Nanoscale Surface Analysis of High Entropy Alloy
Hsin-Hui Huang, Meguya Ryu, Yoshiaki Nishijima +10
Nanoscale surface analysis of 1 micrometer thick high entropy alloys (HEAs) was carried out using nano-IR for hyperspectral imaging and single point spectroscopy in the 700-1700 1/…
High Entropy Alloy under Shock Compression: Optical-Pump X-Ray-Probe
Hsin Hui Huang, Meguya Ryu, Shuji Kamegaki +23
High entropy alloys (HEAs) are multi-principal-element alloys designed for tailorable mechanical performance and have been attracting significant engineering interest, yet their fu…
Structure orientation determined in transmission and reflection: q-plate
Hsin-Hui Huang, Meguya Ryu, Shuji Kamegaki +9
Determination of orientation in the imaged sample/scene has a large application potential when the anisotropy of properties is analysed, usually, under a linearly polarised illumin…