Dislocation interactions and crack nucleation in a fatigued near-alpha titanium alloy
Sudha Joseph, Trevor C Lindley, David Dye
Dislocation interactions at the crack nucleation site were investigated in near-alpha titanium alloy Ti-6242Si subjected to low cycle fatigue. Cyclic plastic strain in the alloy re…
cond-mat.mtrl-sci2018
The mechanisms of hot salt stress corrosion cracking in titanium alloy Ti-6Al-2Sn-4Zr-6Mo
Sudha Joseph, Trevor C Lindley, David Dye +1
Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in…