most citedEarly stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500

^{\circ}

90 citations · 192 across the 5 of their papers we have counts for

collaborators

Showing 2021Show all

2 papers · 1 filter

cond-mat.mtrl-sci2021★ 90 cited

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500 $^{\circ}$ C

Evangelia Charalampopoulou, Konstantina Lambrinou, Tom Van der Donck +8

This work addresses the early stages ( $\leq$ 1000 h) of the dissolution corrosion behavior of 316L and DIN 1.4970 austenitic stainless steels in contact with oxygen-poor (C $_{O}$ < 10$…

cond-mat.mtrl-sci2021★ 20 cited

In situ $H e^{+}$ irradiation of the double solid solution $(T i_{0.5}, Z r_{0.5})_{2} (A l_{0.5}, S n_{0.5}) C$ MAX phase: Defect evolution in the 350-800 °C temperature range

B. Tunca, G. Greaves, J. A. Hinks +3

Thin foils of the double solid solution $(Z r_{0} .5, T i_{0} .5)_{2} (A l_{0.5}, S n_{0.5}) C$ MAX phase were in situ irradiated in a transmission electron microscope (TEM) up to a fluence…

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500∘C

In situ He+ irradiation of the double solid solution (Ti0.5​,Zr0.5​)2​(Al0.5​,Sn0.5​)C MAX phase: Defect evolution in the 350-800 °C temperature range

Early stages of dissolution corrosion in 316L and DIN 1.4970 austenitic stainless steels with and without anticorrosion coatings in static liquid lead-bismuth eutectic (LBE) at 500 $^{\circ}$ C

In situ $H e^{+}$ irradiation of the double solid solution $(T i_{0.5}, Z r_{0.5})_{2} (A l_{0.5}, S n_{0.5}) C$ MAX phase: Defect evolution in the 350-800 °C temperature range