Robust nanopatterning by laser-induced dewetting of metal nanofilms

Abstract

We have observed nanopattern formation with robust and controllable spatial ordering by laser-induced dewetting in nanoscopic metal films. Pattern evolution in Co film of thickness 1\leq h\leq8 nm on SiO_{2} was achieved under multiple pulse irradiation using a 9 ns pulse laser. Dewetting leads to the formation of cellular patterns which evolve into polygons that eventually break up into nanoparticles with monomodal size distribution and short range ordering in nearest-neighbour spacing R. Spatial ordering was attributed to a hydrodynamic thin film instability and resulted in a predictable variation of R and particle diameter D with h. The length scales R and D were found to be independent of the laser energy. These results suggest that spatially ordered metal nanoparticles can be robustly assembled by laser-induced dewetting.

Cited by in corpus (7)

• Investigation of pulsed laser induced dewetting in nanoscopic metal films
• Thickness-dependent spontaneous dewetting morphology of ultrathin Ag films
• Self-organized metal nanostructures through laser driven thermocapillary convection
• Self consistent determination of plasmonic resonances in ternary nanocomposites
• Dynamics of ultrathin metal films on amorphous substrates
• Thermodynamic approach to the dewetting instability in ultrathin films
• On efficient asymptotic modelling of thin films on thermally conductive substrates