The effect of Zn substitution on the state of oxygen deficiency and hole concentration in Y1-xCaxBa2(Cu1-yZny)3O7-d
arXiv:cond-mat/0601564 · doi:10.1016/j.physc.2006.04.101
Abstract
We have investigated the effect of Zn substitution on the hole content, p, and the oxygen deficiency, d, for a series of high-quality crystalline c-axis oriented thin films and polycrystalline Y1-xCaxBa2(Cu1-yZny)3O7-delta compounds over a wide range of composition (x, y, and delta). p was determined from the room-temperature thermopower, S[290K]. When annealed at a given temperature and oxygen partial pressure, a small but systematic variation in S[290K] was observed with Zn, for all the samples. From the analysis of the temperature derivative of resistivity, drho/dT, at 300K, which varies almost linearly with p, irrespective of the composition of the sample, and the thermo-gravimetric analysis (TGA), we have found that annealing under identical conditions makes the Zn-substituted compounds somewhat more oxygen deficient compared to the Zn-free ones.
Cited by in corpus (4)
- Unified electronic phase diagram for hole-doped high-Tc cuprates
- Effect of Zn substitution on the suppression of Tc of Y1-xCaxBa2(Cu1-yZny)3O7-delta superconductors: pseudogap and the systematic shift of the optimum hole content
- Critical current density of hole doped high-Tc cuprates and heavy fermion superconductors: relevance to the possible quantum critical behavior
- Estimation of Cooper pair density and its relation to the critical current density in hole doped high-Tc cuprate superconductors