Intergranular pinning potential and critical current in the magnetic superconductor RuSr2Gd1.5Ce0.5Cu2O10
arXiv:cond-mat/0410396 · doi:10.1103/PhysRevB.71.064520
Abstract
The intergranular pinning potential U and the critical current density Jc for polycrystalline RuSr2Gd1.5Ce0.5Cu2O10 ruthenate-cuprate were determined at zero magnetic field and temperature through the frequency shift in the peak of the imaginary part of the ac magnetic susceptibility, X". A critical state model, including a flux creep term, was found to accurately describe the X" behavior. The obtained values, U(H=0,T=0) ~ 30 meV and Jc(H=0,T=0) ~ 110 A/cm^2 are about two orders of magnitude and four times lower, respectively, in comparison with the high-Tc cuprate YBa2Cu3O7. These results were ascribed to the effects of the Ru magnetization on the connectivity of the weak-linked network, giving an intrinsic local field at the junctions of ~ 15 Oe. The impact on Jc is less intense because of the small average grain radius (~1 micrometer). The intragranular London penetration length at T = 0, [lambda_L(0) ~ 2 micrometer], was derived using a Kim-type expression for the field dependence of Jc. A possible source for the large value of lambda_L in comparison to the high-Tc cuprates is suggested to come from a strong intragrain granularity, due to structural domains of coherent rotated RuO6 octahedra separated by antiphase boundaries.
5 pages, 3 figures. To appear in Physical Review B