Gallium vacancy and the residual acceptor in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Abstract

Positron lifetime, Photoluminescence and Hall measurements were performed to study undoped p-type gallium antimonide materials. A 314ps lifetime component, attributed to $V_{Ga}$ related defect, was identified in the positron lifetime measurement. In the PL measurement, a $778meV$ and a $797meV$ peaks were observed. Isochronal annealing studies were performed and at the temperature of $300^{o}C$, both the 314ps positron lifetime component and the two PL signals disappeared, which gives a clear and strong evidence for their correlation. However, the hole concentration ($\sim 2\times 10^{17}c{m}^{-3}$) was observed to be constant throughout the whole annealing temperature range up to $500^{o}C$. Contradictory to general belief, this implies, at least for samples with annealing temperatures above $300^{o}C$, the Ga vacancy is not the acceptor responsible for the p-type conduction.

3 pages, 3 figures