Unusual magnetic relaxation behavior in La0.5Ca0.5MnO3 and Nd0.5Sr0.5MnO3

Abstract

We have carried out a systematic magnetic relaxation study, measured after applying and switching off a 5 T magnetic field to polycrystalline samples of La0.5Ca0.5MnO3 and Nd0.5Sr0.5MnO3. The long time logarithmic relaxation rate (LTLRR), decreased from 10 K to 150 K and increased from 150 K to 195 K in La0.5Ca0.5MnO3. This change in behavior was found to be related to the complete suppression of the antiferromagnetic phase above 150 K and in the presence of a 5 T magnetic field. At 195 K, the magnetization first decreased, and after a few minutes increased slowly as a function of time. Moreover, between 200 K and 245 K, the magnetization increased throughout the measured time span. The change in the slope of the curves, from negative to positive at about 200 K was found to be related to the suppression of antiferromagnetic fluctuations in small magnetic fields. A similar temperature dependence of the LTLRR was found for the Nd0.5Sr0.5MnO3 sample. However, the temperature where the LTLRR reached the minimum in Nd0.5Sr0.5MnO3 was lower than that of La0.5Ca0.5MnO3. This result agrees with the stronger ferromagnetic interactions that exist in Nd0.5Sr0.5MnO3 in comparison to La0.5Ca0.5MnO3. The above measurements suggested that the general temperature dependence of the LTLRR and the underlying physics were mainly independent of the particular charge ordering system considered. All relaxation curves could be fitted using a logarithmic law at long times. This slow relaxation was attributed to the coexistence of ferromagnetic and antiferromagnetic interactions between Mn ions, which produced a distribution of energy barriers.

Accepted to PRB as a regular article, 10 figures, Scheduled Issue: 01 June 2001

Cited by in corpus (11)

• Magnetodielectric consequences of phase separation in the colossal magnetoresistance manganite Pr0.7Ca0.3MnO3
• Magnetic relaxation in La0.250Pr0.375Ca0.375MnO3 with varying phase separation
• Magnetization studies of phase separation in La${}_{0.5}$Ca${}_{0.5}$MnO${}_3$
• Specific heat and magnetic measurements in Nd0.5Sr0.5MnO3, Nd0.5Ca0.5MnO3 and Ho0.5Ca0.5MnO3 samples
• Specific heat at low temperatures and magnetic measurements in Nd0.5Sr0.5MnO3 and R0.5Ca0.5MnO3 (Nd, Sm, Dy and Ho) samples
• Glassy behavior in the ferromagnetic and the non-magnetic insulating states of the rare earth manganates, Ln0.7Ba0.3MnO3 (Ln = Nd or Gd)
• Critical exponents and the correlation length in the charge exchange manganite spin glass Eu_{0.5}Ba_{0.5}MnO_{3}
• Resistive relaxation in field-induced insulator-metal transition of a (La${}_{0.4}$Pr${}_{0.6}$)${}_{1.2}$Sr${}_{1.8}$Mn${}_2$O${}_7$ bilayer manganite single crystal
• Stretched exponential behavior in remanent lattice striction of a (La,Pr)${}_{1.2}$Sr${}_{1.8}$Mn${}_2$O${}_7$ bilayer manganite single crystal
• Study of magnetic and specific heat measurements at low temperatures in Nd0.5Sr0.5MnO3 and Nd0.5Ca0.5MnO3
• The dynamics of magnetization in phase separated manganite around half doping: a case study for Pr${}_{0.5}$Sr${}_{0.5}$Mn${}_{0.925}$Ga${}_{0.075}$O${}_3$