Fracture initiation in silicate glasses via a universal shear localization mechanism

Abstract

Shear bands lie at the root of fracture initiation in bulk metallic glasses and amorphous polymers. For silicate glasses, in contrast, studies have largely emphasized permanent volumetric strain, commonly referred to as densification. Here we systematically investigate indentation-induced fracture in two distinct families of aluminoborosilicate glasses. The results demonstrate that plastic shear flow plays a decisive role in governing fracture initiation. In addition, molecular dynamics simulations reveal a pronounced composition dependence of softening associated with plastic shear flow, closely mirroring the experimentally observed propensity for strain localization. We conclude that silicate glasses conform to a universal pattern of rupture initiation governed by localization of shear-deformation, aligning with a broad range of amorphous materials, including bulk metallic glasses and glassy polymers.

References in corpus (10)

• Strain localization and percolation of stable structure in amorphous solids
• A random critical point separates brittle and ductile yielding transitions in amorphous materials
• Predicting plasticity in disordered solids from structural indicators
• New optimization scheme to obtain interaction potentials for oxide glasses
• Shear banding in metallic glasses described by alignments of Eshelby quadrupoles
• Rejuvenation and Shear-Banding in model amorphous solids
• Yielding and plasticity in amorphous solids
• New interaction potentials for alkaline earth silicate and borate glasses
• Brittleness of metallic glasses dictated by their state at the fragile-to-strong transition temperature
• Unveiling the Asymmetry in Density within the Shear Bands of Metallic Glasses