Stabilization of the first-order phase transition character and Enhancement of the Electrocaloric Effect by NBT substitution in BaTiO${}_3$ ceramics

Abstract

The electrocaloric properties of BaTiO${}_3$-based lead-free ferroelectric materials have been widely investigated. One approach to achieving a large electrocaloric response is to exploit the substantial polarization change associated with the first-order phase transition at the Curie temperature. Following this strategy, we investigated the electrocaloric response of (1$-x$)BaTiO${}_3$-$x$Na${}_{0.5}$Bi${}_{0.5}$TiO${}_3$ (BT-NBT) ceramics for x = 0.05, 0.10, 0.20, and 0.30. In this BT-rich region of the solid solution, it is established that increasing the NBT content enhances the tetragonality of BaTiO${}_3$. We show that this increase in tetragonality helps maintain the first-order nature of the phase transition and enables a correspondingly large electrocaloric response, despite the simultaneous enhancement of relaxor ferroelectric character with NBT substitution. A significantly large effective electrocaloric temperature change ($\Delta T_{\mathrm{eff}}$) of ~1.65 K was obtained for the x = 0.20 composition under an applied field of 40 kV/cm using direct electrocaloric measurements, in reasonable agreement with the indirect results.

accepted version of the article published in J. Mater. Chem. C. 10 Pages, 7 Figures. Plus SI file as a single pdf