Size selection of crack front defects: Multiple fracture-plane interactions and intrinsic lengthscales

Abstract

Material failure is mediated by the propagation of cracks, which in realistic 3D materials typically involve multiple coexisting fracture planes. Multiple fracture-plane interactions create poorly understood out-of-plane crack structures, such as step defects on tensile fracture surfaces. Steps form once a slowly moving, distorted crack front segments into disconnected overlapping fracture planes separated by a stabilizing distance $h_{\max }$. Our experiments on numerous brittle hydrogels reveal that $h_{\max }$ varies linearly with both a nonlinear elastic length $\Gamma (v)/\mu$ and a dissipation length $\xi$. Here, $\Gamma (v)$ is the measured crack velocity $v$-dependent fracture energy and $\mu$ is the shear modulus. These intrinsic lengthscales point the way to a fundamental understanding of multiple-crack interactions in 3D that lead to the formation of stable out-of-plane fracture structures.

5 pages, 5 figures + supplementary materials + bibliographical list. See related work at: https://doi.org/10.48550/arXiv.2403.17781

References in corpus (8)

• The Breakdown of Linear Elastic Fracture Mechanics near the Tip of a Rapid Crack
• Instability in dynamic fracture and the failure of the classical theory of cracks
• Weakly Nonlinear Theory of Dynamic Fracture
• Magic angles and cross-hatching instability in hydrogel fracture
• Configurational stability of a crack propagating in a material with mode-dependent fracture energy - Part I: Mixed-mode I+III
• How hidden 3D structure within crack fronts reveals energy balance
• Nonlinear focusing in dynamic crack fronts and the micro-branching transition
• Quenched disorder and instability control dynamic fracture in three dimensions