Refining microstructures in additively manufactured Al/Cu gradients through TiB${}_2$ inclusions

Abstract

The additive manufacture of compositionally graded Al/Cu parts by laser engineered net shaping (LENS) is demonstrated. The use of a blue light build laser enabled deposition on a Cu substrate. The thermal gradient and rapid solidification inherent to selective laser melting enabled mass transport of Cu up to 4 mm away from a Cu substrate through a pure Al deposition, providing a means of producing gradients with finer step sizes than the printed layer thicknesses. Printing graded structures with pure Al, however, was prevented by the growth of Al${}_2$Cu${}_3$ dendrites and acicular grains amid a matrix of Al${}_2$Cu. A combination of adding TiB${}_2$ grain refining powder and actively varying print layer composition suppressed the dendritic growth mode and produced an equiaxed microstructure in a compositionally graded part. Material phase was characterized for crystal structure and nanoindentation hardness to enable a discussion of phase evolution in the rapidly solidifying melt pool of a LENS print.

In review at JOM