Origin of superconductivity in tungsten thin films

Abstract

The most common allotrope of tungsten, α-W, has a superconducting transition at a temperature of ~11 mK. However, two other forms of tungsten have been reported to have superconducting transitions in the temperature range Tc ~ 2-5 K when synthesized as thin films: Crystalline \b{eta}-W and amorphous W (a-W). In this work we carry out a systematic study of W films synthesized using d.c. magnetron sputtering, using transport, low frequency magnetic shielding response, and transmission electron microscopy. Our results show that while a-W is indeed a bulk superconductor, superconductivity in \b{eta}-W probably originates from an amorphous phase that forms along with the \b{eta}-W phase. Our findings reconcile some of the anomalies earlier reported in \b{eta}-W, such the very small superconducting gap and the decrease of Tc with increase in film thickness.

References in corpus (6)

• Nanoscale superconducting properties of amorphous W-based deposits grown with focused-ion-beam
• Two step disordering of the vortex lattice across the peak effect in a weakly pinned Type II superconductor, Co0.0075NbSe2
• Superconductivity in nanocrystalline tungsten thin films growth by sputtering in a nitrogen-argon mixture
• Structure and dynamics of a pinned vortex liquid in superconducting a-Re_xZr (x ~ 6) thin film
• Magnetic field induced transition from a vortex liquid to Bose metal in ultrathin a-MoGe thin film
• Anomalously small superconducting gap in the strong spin-orbit coupled superconductor: $\beta -$Tungsten

Cited by in corpus (6)

• A compact inertial nano-positioner operating at cryogenic temperatures
• Detailed Analysis of the Superconducting Gap with Dynes Pair-Breaking Scattering
• Growth Optimization of MoSi Thin Film and Measurement of Transport Critical Current Density of its Meander Structure
• Fermi surface origin of the low-temperature magnetoresistance anomaly
• Scanning tunneling spectroscopy of superconducting nitridized aluminum thin films
• Effect of Deposition Pressure on the Superconductivity of Ti40V60 Alloy Thin Films