Effect of Pb addition on microstructure, transport properties and the critical current density in a polycrystalline FeSe0.5Te0.5

Abstract

We have investigated the effects of lead (Pb) additions (x) up to 40 wt.% (x = 0-0.4) on the structure, electrical properties, and magnetic properties of FeSe0.5Te0.5 superconductor. The samples were prepared by the solid-state reaction method and characterized by various techniques. The parent compound (x = 0) showed the onset temperature Tc onset of 15 K, and zero-resistance temperature, Tc offset of 12 K. The addition of Pb enhances the metallic characteristics of FeSe0.5Te0.5, but both Tc onset and Tc offset are decreased to the lower temperature with the broadened transition width. The Tc onset is nearly the same (10.3 K) at higher additions, such as x = 0.3 and 0.4, but zero resistivity is not observed up to 7 K. Microstructural analysis and transport studies suggest that for x > 0.05, Pb additions weakened the coupling between grains and suppressed the superconducting percolation, leading to a broad transition. More importantly, the inclusion of a relatively small amount of Pb (x = 0.05) increased the critical current density, Jc, in the entire magnetic field, which might be attributable to better phase uniformity as well as good grain connectivity.

References in corpus (9)

• Tellurium substitution effect on superconductivity of the alpha-phase Iron Selenide
• Bulk Superconductivity at 14 K in Single Crystals of Fe1+yTexSe1-x
• Substitution Effects on FeSe Superconductor
• A review of Fe-chalcogenide superconductors: the simplest Fe-based superconductor
• Metal - Insulator transition in Fe1.01-xCuxSe
• Combined microstructural and magneto optical study of current flow in polycrystalline forms of Nd and Sm Fe-oxypnictides
• Enhanced superconducting properties in FeCr${}_x$Se
• Effect of 3d Metal (Co and Ni) Doping on the Superconductivity of FeSe0.5Te0.5
• The drastic effect of the impurity scattering on the electronic and superconducting properties of Cu-doped FeSe

Cited by in corpus (4)

• High-pressure synthesis and the enhancement of the superconducting properties of FeSe0.5Te0.5
• Cometal addition effect on superconducting properties and granular behaviours of polycrystalline FeSe0.5Te0.5
• Comparison of Gd addition effect on the superconducting properties of FeSe0.5Te0.5 bulks under ambient and high-pressure conditions
• High-pressure growth effect on the properties of high-Tc iron-based superconductors: A short review