Spin-phonon interactions and magnetoelectric coupling in Co${}_4$$B_2$O${}_9$ ($B$ = Nb, Ta)

Abstract

In order to explore the consequences of spin-orbit coupling on spin-phonon interactions in a set of chemically-similar mixed metal oxides, we measured the infrared vibrational properties of Co${}_4{B}_2$O${}_9$ ($B$ = Nb, Ta) as a function of temperature and compared our findings with lattice dynamics calculations and several different models of spin-phonon coupling. Frequency vs. temperature trends for the Co${}^{2+}$ shearing mode near 150 cm${}^{-1}$ reveal significant shifts across the magnetic ordering temperature that are especially large in relative terms. Bringing these results together and accounting for noncollinearity, we obtain spin-phonon coupling constants of -3.4 and -4.3 cm${}^{-1}$ for Co${}_4$Nb${}_2$O${}_9$ and the Ta analog, respectively. Analysis reveals that these coupling constants derive from interlayer (rather than intralayer) exchange interactions and that the interlayer interactions contain competing antiferromagnetic and ferromagnetic contributions. At the same time, beyond-Heisenberg terms are minimized due to fortuitous symmetry considerations, different than most other 4$d$- and 5$d$-containing oxides. Comparison with other contemporary oxides shows that spin-phonon coupling in this family of materials is among the strongest ever reported, suggesting an origin for magnetoelectric coupling.

References in corpus (6)

• Magnetic-induced phonon anisotropy in ZnCr${}_2$O${}_4$ from first principles
• Direct visualization of Rashba-split bands and spin/orbital-charge interconversion at KTaO${}_3$ interfaces
• Spin phonon coupling in frustrated magnet CdCr${}_2$O${}_4$
• Experimental and first-principles studies of magnetism and magnetoelectric effect in Co4Nb2O9 and Co4Ta2O9
• Observation of spin-orbit magnetoresistance in metallic thin films on magnetic insulators
• Investigation of spin-phonon coupling and local magnetic properties in magnetoelectric Fe2TeO6

Cited by in corpus (1)

• Contrasting magnetothermal conductivity in sibling Co-based honeycomb-lattice antiferromagnets