Evidence of Strong Dzyaloshinskii-Moriya Interaction at the Cobalt/Hexagonal Boron Nitride Interface

Abstract

The Dzyaloshinskii-Moriya interaction (DMI) and perpendicular magnetic anisotropy (PMA) were measured on four series of Co films (1-2.2 nm thick) grown on Pt or Au and covered with h-BN or Cu. Clean h-BN/Co interfaces were obtained by exfoliating h-BN and transferring it onto the Co film in situ in the ultra-high-vacuum evaporation chamber. By comparing h-BN and Cu-covered samples, the DMI induced by the Co/h-BN interface was extracted and found to be comparable in strength to that of the Pt/Co interface, one of the largest known values. The strong observed DMI despite the weak spin-orbit interaction in h-BN supports a Rashba-like origin in agreement with recent theoretical results. Upon combination of it with Pt/Co in Pt/Co/h-BN heterostructures, even stronger PMA and DMI are found which stabilizes skyrmions at room temperature and a low magnetic field.

References in corpus (9)

• Electric Field Effect in Atomically Thin Carbon Films
• Advances in the Physics of Magnetic Skyrmions and Perspective for Technology
• Interfacial Dzyaloshinskii-Moriya interaction in perpendicularly-magnetized Pt/Co/AlO${}_x$ ultrathin films measured by Brillouin light spectroscopy
• Control of nonlocal magnon spin transport via magnon drift currents
• Rashba-type Dzyaloshinskii-Moriya interaction, perpendicular magnetic anisotropy and skyrmion states at 2D materials/Co interfaces
• Interfacial Dzyaloshinskii-Moriya interaction and spin-orbit torque in Au1-xPtx/Co bilayers with varying interfacial spin-orbit coupling
• Element-selective modulation of interfacial Dzyaloshinskii-Moriya interaction in Pt|Co|Metal based multilayers
• Making the Dzyaloshinskii-Moriya interaction visible
• Nature of Interfacial Dzyaloshinskii-Moriya Interactions in Graphene/Co/Pt(111) Multilayer Heterostructures