Metallization of hydrogen by intercalating ammonium ions in metal fcc lattices at low pressure

Abstract

Metallic hydrogen is capable of showing room temperature superconductivity, but its experimental syntheses are extremely hard. Therefore, it is desirable to reduce the synthesis pressure of metallic hydrogen by adding other chemical elements. However, for most hydrides, the metallization of hydrogen by "chemical precompression" to achieve high-temperature superconductivity still requires relatively high pressure, making experimental synthesis difficult. How to achieve high-temperature superconductivity in the low-pressure range (0-50 GPa) is a key issue for realizing practical applications of superconducting materials. Toward this end, this work proposes a strategy for inserting ammonium ions in the fcc crystal of metals. High-throughput calculations of the periodic table reveal 12 elements which can form kinetically stable and superconducting hydrides at low pressures, where the highest superconducting transition temperatures of AlN2H8, MgN2H8 and GaN2H8 can reach up to 118.40, 105.09 and 104.39 K. Pressure-induced bond length changes and charge transfer reveal the physical mechanism of high-temperature superconductivity, where the H atom continuously gains electrons leading to the transition of H+ ions to atomic H, facilitating metallization of hydrogen under mild pressure. Our results also reveal two strong linear scalar relationships, one is the H-atom charge versus superconducting transition temperature and the other is the first ionization energy versus the highest superconducting transition temperature. Besides, ZnN2H8, CdN2H8, and HgN2H8 were found to be superconductors at ambient pressure, and the presence of interstitial electrons suggests that they are also electrides, whose relatively low work functions (3.03, 2.78, and 3.05 eV) imply that they can be used as catalysts for nitrogen reduction reactions as well.

References in corpus (6)

• Quantum ESPRESSO: a modular and open-source software project for quantum simulations of materials
• Observation of the Wigner-Huntington Transition to Solid Metallic Hydrogen
• LaBH${}_8$: the first high-T${}_c$ low-pressure superhydride
• Prediction of high-Tc superconductivity in ternary lanthanum borohydrides
• Phonon-mediated high-temperature superconductivity in ternary borohydride KB${}_2$H${}_8$ around 12 GPa
• Tuning Chemical Precompression: Theoretical Design and Crystal Chemistry of Novel Hydrides in the Quest for Warm and Light Superconductivity at Ambient Pressures

Cited by in corpus (4)

• Stabilizing a hydrogen-rich superconductor at 1 GPa by the charge-transfer modulated virtual high-pressure effect
• Theoretical Predictions of MB5N5: Atom-Stuffed Boronitride Clathrate Cages Derived from the High-Pressure Superhydride
• Appraising the absolute limits of nanotubes and nanospheres to preserve high-pressure materials
• Composition-Based Machine Learning for Screening Superconducting Ternary Hydrides from a Curated Dataset