Optical properties of Au-Hf thin films

Abstract

The optical properties of thin films of intermetallic Au${}_3$Hf were experimentally investigated for the first time, which display clear plasmonic properties in the optical and near infrared region with negative permittivity. In contrast to similar alloys, such as films of Au${}_3$Zr, the films express more negative ${\epsilon }^{\prime }$ values and lower ${\epsilon }^{\prime \prime }$ values across most of the wavelengths (370-1570 nm) investigated. The Au${}_3$Hf films were fabricated by DC magnetron sputtering at a range of deposition temperatures, from room temperature to 415${}^o$C, and annealed at different vacuum levels. The films mostly formed as a combination of Au${}_3$Hf, Au${}_2$Hf and Au${}_4$Hf phases when deposited below 400${}^o$C, and exclusively Au${}_3$Hf phase at above 400${}^o$C, indicating key conditions for isolating this phase. The films were stable when annealed at 10${}^{-8}$ Torr, but when annealed again at 10${}^{-6}$ Torr the films oxidised and changed into a mix of Au- Hf phases, suggesting resistance to oxidization may be an issue for un-encapsulated applications at elevated temperatures.

arXiv comment19 pages, including references, plus 3 pages of supplementary material. 8 figures and 1 table in main text, 1 figure and 1 table in supplementary material